Incorporation Of Ag Nanowires In Cuwo4 For Improved Visible Light-Induced Photoanode Performance

We report the sol-gel synthesis of a CuWO4 (E-g similar to 2.0-2.15 eV) thin film loaded with Ag nanowires. The incorporation of Ag nanowires into the semiconductor matrix significantly improves the performance of CuWO4 as a photoanode for use in photochemical water splitting (PEC). Here, we have developed a planar electrode to test the photoactivity of the catalyst using standard electrochemical procedures under simulated solar light. The sol-gel synthesis of CuWO4 is modified such that we add Ag nanowires during sol aging. We demonstrate that there is negligible change to the CuWO4 matrix microstructure, morphology or crystal structure. When we compare the pristine CuWO4 to the material with Ag nanowires embedded in the CuWO4 matrix there is a fourfold improvement of photocurrent at 1.23 V vs. NHE to ca. 1.5 mA cm(-2) (pH 9) under simulated AM1.5G illumination. This photocurrent is very competitive against more well developed photoanode structures when consideration for surface area is allowed. The Ag nanowires increase carrier mobility film enabling a sufficiently thick sample of catalyst, measured at 750 nm, to effectively harvest incident light. The addition of the Ag nanowires removes the plateau region found for CuWO4 further indicating that there is a good flow of carriers to the surface of the catalyst, a significant improvement as carrier mobility has been shown to be low in CuWO4. The Faradaic efficiency of the catalyst was measured at 31%. Our flat band potential is found to be 0 vs. NHE. The ability to make a highly photoactive catalyst using a simple chemical process opens up opportunities in a wide range of areas that focus on PEC and other light harvesting processes.