Nano-Welding of Ag Nanowires Using Rapid Thermal Annealing for Transparent Conductive Films.

Ag nanowire (NW) films obtained by the spraying the Ag NWs on the substrates were nano-welded by rapid thermal annealing (RTA) process and the effect of RTA process on the change of sheet resistance and optical transmittance of the Ag NW films was investigated. The increased number of Ag NW sprays on the substrate decreased the sheet resistance but also decreased the optical transmittance. By the annealing for 60 sec in a nitrogen environment to 225-250 degrees C, the sheet resistance of Ag NW film could be decreased to about 50%, even though it was accompanied by the slight decrease of optical transmittance less than 5%. The decrease of sheet resistance was related to the nano-welding of the Ag NW junctions and the slight decrease of optical transmittance was related local melting of the Ag NWs and spreading on the substrate surface. Through the nano-welding by RTA process, the Ag NW film with the sheet resistance of similar to 20 Omega/sq. and the optical transmittance of 93% could be obtained.