The gamma irradiation of PBO fiber on the mechanical and tribological properties of PTFE composites

The mechanical and tribological behavior of gamma irradiated poly(p-phenylene benzobisoxazole) (PBO) fiber filled polytetrafluoroethylene (PTFE) composites was investigated. The gamma irradiated PBO fiber composite had the highest inter-laminar shear strength value of all the combinations because its higher bond strength may have hindered a large fiber/matrix debonding. X-ray photoelectron spectroscopy results indicate that the contents of polar groups on the surface of gamma irradiated PBO fiber increase compared to PBO fiber. The wear tests were conducted on a ring-on-block apparatus using composite block against polished metal counterparts under dry sliding conditions. It can also be found that gamma irradiation treatment was helpful to the improvement of the anti-wear ability of the PTFE composite which was related to the abrasive wear mechanism.