Failure analysis of the flash evaporator in an alumina production plant
Case Studies in Engineering Failure Analysis(2013)
摘要
•The failure cause of a flash evaporator was investigated.•Uniform corrosion was not the main cause.•Many branch cracks which propagated intergranularly were observed.•Failure of the flash evaporator was caused by caustic embrittlement.•The necessary conditions for caustic embrittlement were satisfied.
更多查看译文
关键词
Flash evaporator,Failure analysis,Caustic embrittlement,Weld