Effects of deformation ratio above recrystallizaton temperature on microstructure and properties of 2A12 aluminum alloy
ADVANCED MATERIALS AND PROCESS TECHNOLOGY, PTS 1-3(2012)
摘要
The thermomechanical treatment of a 2A12 aluminum alloy was researched and the influence of deformation ratio above recrystallization temperature on microstructure and hardness was analyzed emphatically. The result reveals that when the deformation ratio is low at first, the hardness of specimen decreased because the effect of recrystallization softening overwhelms the effect of deformation strengthening. However, hardness increased with increasing deformation ratio. In addition, the microstructure became more homogeneous and grains were refined obviously by metallography microscope observation with increasing deformation ratio. The second phase precipitates dispersedly to strengthen the alloy.
更多查看译文
关键词
2A12 aluminum alloy,Thermomechanical treatment,deformation ratio above recrystallization temperature,microstructure,hardness
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要