Gallium Vacancy And The Residual Acceptor In Undoped Gasb Studied By Positron Lifetime Spectroscopy And Photoluminescence

APPLIED PHYSICS LETTERS(2002)

引用 27|浏览8
暂无评分
摘要
Positron lifetime, photoluminescence (PL), and Hall measurements were performed to study undoped p-type gallium antimonide materials. A 314 ps positron lifetime component was attributed to Ga vacancy (V-Ga) related defect. Isochronal annealing studies showed at 300 degreesC annealing, the 314 ps positron lifetime component and the two observed PL signals (777 and 797 meV) disappeared, which gave clear and strong evidence for their correlation. However, the hole concentration (similar to2x10(17) cm(-3)) was observed to be independent of the annealing temperature. Although the residual acceptor is generally related to the V-Ga defect, at least for cases with annealing temperatures above 300 degreesC, V-Ga is not the acceptor responsible for the p-type conduction. (C) 2002 American Institute of Physics.
更多
查看译文
关键词
kinetics,physics engineering
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要