Textured PbTiO₃ Based Ceramics Fabricated by Slip Casting in a High Magnetic Field

Yasunari Miwa,Shinichiro Kawada,Masahiko Kimura,Yukio Higuchi,Hiroshi Takagi,Tohru S. Suzuki,Tetsuo Uchikoshi,Yoshio Sakka

Key Engineering Materials（2010）

引用 2|浏览7

暂无评分

摘要

Textured PbTiO3 (PT) ceramics were fabricated by slip casting in a high magnetic field of 12 T. The sample obtained from the powder calcined at 1100 degrees C was (100), (010), and (001)-oriented, and the orientation factor was 90 %. On the other hand, the sample obtained from the powder calcined at 900 degrees C was not oriented. Aggregability and crystallinity of powder are an important factor when textured ceramics are fabricated by slip casting in a high magnetic field.

查看译文

关键词

orientation method,perovskite,aggregability,crystallinity