Effect of boron substitution on the properties of NiZnCu ferrite for multilayer chip inductors
Thin Solid Films(2011)
摘要
The initial permeability of the toroidal core sample with boron substituted NiZnCu ferrite (Ni0.36Zn0.44Cu2.2Fe1.96−xBxO4(x=0.0, 0.2, 0.4, 0.6, and 0.8)) which was annealed at 900°C for 2h decreased from 162.4 to 123.2 as boron concentration x is increased from 0.2 to 0.8. The quality factor and density of 0.2mol% boron substituted NiZnCu ferrites sintered at 900°C for 2h was about 240.0 and 4.84g/cm3, respectively. The density, shrinkage and saturation magnetization were increased with increasing annealing temperature. It was shown that the boron substituted NiZnCu ferrite systems were promising as a high quality factor material in the fabrication of multilayer chip inductors (MLCIs).
更多查看译文
关键词
NiZnCu ferrite,Multilayer chip inductors,Toroidal core