Photoluminescent multilayer films based on polyoxometalatesXRR spectrum of {(PEI/PSS/PAH)(EuP5W30/PAH)6}, UV-Vis spectrum of EuP5W30 anion and AFM image of the top layer of (PEI/PSS/PAH). See http://www.rsc.org/suppdata/jm/b1/b108283c/

Ultrathin multilayer films consisting of the polyoxotungstoeuropate cluster K-12[EuP5W30O110] (EuP5W30) and poly( allylamine hydrochloride) (PAH) have been prepared by the layer-by-layer self-assembly method. The (EuP5W30 /PAH) multilayer films have been characterized by small-angle X-ray reflectivity measurements, X-ray photoelectron spectra, and atomic force microscopy (AFM). From the AFM images, the thickness of the {PEI/PSS/PAH(EuW30/PAH)} multilayer film was estimated to be 6.5 nm, corresponding to an average thickness of ca. 1.1 nm for a EuW30/PAH layer pair. The photoluminescent behavior of the film at room temperature was investigated to show the characteristic Eu3+ emission pattern of D-5(0)-->F-7(J). The fluorescence behavior of the multilayer film is essentially identical to that of H-n[EuP5W30O110]((12-n)-) in a concentrated aqueous solution, except for the relative intensities and peak bandwidths. The occurence of photoluminescent activity confirms the potential for creating luminescent multilayers with polyoxometalates (see ref. 23).