Effect of powder painting procedures on the filiform corrosion of aluminium profiles

In this work, the filiform corrosion behaviour of powder painted aluminium profiles was studied, and the coating barrier properties together with adhesion to the substrate were analysed. Samples coated with a traditional painting procedure (one powder layer application followed by curing), and other samples coated using a special cycle to obtain wood grain effect were compared using accelerated filiform corrosion tests. Moreover, in order to better understand the degradation mechanisms of painted metal substrates, thermal stresses were applied to accelerate the natural weathering. The effects of the thermal aging were analysed by electrochemical impedance spectroscopy.