Interstitial atom clustering at 57Co impurity atoms in aluminium after electron and neutron irradiation

W. Mansel, H. Meyer, G. Vogl

RADIATION EFFECTS AND DEFECTS IN SOLIDS(2006)

引用 37|浏览3
暂无评分
摘要
Abstract From Mossbauer measurements on Al 57Co samples irradiated above stage I with 2.8 MeV electrons it is found that the temperature dependence of the Debye-Waller factor of 57Co impurities having trapped interstitials becomes weaker with increasing number of interstitials trapped at a 57Co atom. This behaviour is explained by a linear superposition of two phenomena: The dynamics of 57Co impurities with only one trapped interstitial (mixed dumbbell) is determined by jumps in an octahedral cage. When two or more interstitials are trapped, the cage jumps are suppressed and the mixed dumbbells can only perform low frequency vibrations. The temperature dependence of the Debye-Waller factor was used to pursue the clustering of interstitials at 57Co impurities in aluminium after fast neutron irradiation at 4.6 K (dose 0.7 × 1018 cm−2) as well as after isochronal annealing. We found that after irradiation cobalt impurities have trapped interstitial clusters. Annealing in stage 1 leads to substantial fraction...
更多
查看译文
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要